Sikapower 1200
|
|
Còn hàng
- High fatigue and impact resistance
- Long open time at high temperature and humidity
- Cures at room temperature
- Accelerated curing and higher mechanical strength with heat
- Good adhesion to fiber-reinforced plastics
- Does not contain solvents or PVC
Thương hiệu:
SikaPower®-1200 is a tough, high strength, solvent free, thixotropic, fast curing epoxy adhesive. It is designed for fast assembly bonding of structural composite substrates, like GFRP and CFRP laminates, as well as metallic substrates. The adhesive cures by polyaddition of the two components.
| Properties |
|
|||||
| Chemical base |
|
|||||
| Color (CQP001-1) | mixed |
|
||||
| Tỉ trọng | mixed, calculated |
|
||||
| Mixing ratio | A:B by volume A:B by weight | 100:50 100:54 | ||||
| Hàm lượng chất rắn | 100 % | |||||
| Viscosity (CQP029-4) | at 10 s-1 |
|
||||
| Consistency | Thixotropic paste | |||||
| Application temperature | 15 ─ 30 °C | |||||
| Open time (CQP046-11 / ISO 4587) | 45 min B, C, D | |||||
| Curing time (CQP046-9, ISO4587) | at 23 °C at 70 °C | 48 hours 2 hours | ||||
| Tensile strength (CQP543-1 / ISO 527) | 40 MPa C, E | |||||
| E-Modulus (CQP543-1 / ISO 527) | 2600 MPa C, E | |||||
| Elongation at break (CQP543-1 / ISO 527) | 3.5 % C, E | |||||
| Tensile lap-shear strength (CQP046-9 / ISO 4587) | 20 MPa C, D, E | |||||
| Critical stress intensity factor KIc (ISO 13586) | 2.7 m1/2 MPa C, E, F | |||||
| Critical energy release rate GIc (ISO 13586) | 3.5 N/mm C, E, F | |||||
| Glass transition temperature (CQP509-1 / ISO 6721) | 90 °C E | |||||
| Hạn sử dụng | drum cartridges | 12 months G 24 tháng G |